Overview631 stainless steel, also known as 17-7 PH stainless steel, is a versatile corrosion-resistant alloy ...    More ...

Overview

---

631 stainless steel, also known as 17-7 PH stainless steel, is a versatile corrosion-resistant alloy with a unique chemical composition. The main components are iron, chromium and nickel, but also contain small amounts of aluminum and copper. 631 stainless steel is unique in its unique precipitation hardening ability achieved through heat treatment. This stainless steel alloy is widely used in various industries, including aerospace, automotive and medical. Its superior strength combined with good formability makes it suitable for the manufacture of complex components such as springs, washers and high-strength structural parts. In addition, its corrosion resistance and biocompatibility make it an excellent choice for surgical instruments, orthodontic devices, and implantable medical devices. With its combination of mechanical properties and resistance to environmental factors, 631 stainless steel remains a popular material in a variety of demanding applications.
Chemical composition

---

CMnSiPSCrNiAl
0.0910.50.0250.02516.00 – 17.256.50 – 7.750.75 – 1.25

Mechanical Properties

---

AISI 63
Ultimate Tensile
Strength1170Mpa,170000psi
Yield Strength965Mpa,140000ps
Elongation %6 min

Physical propertiesTensile strength σb (MPa) : solid solution,≤1030; Aging at 565℃,≥1140; Aging at 510℃ ≥1230Conditional yield strength σ0.2 (MPa) : solid solution,≤380; Aging at 565℃,≥960; Aging at 510℃ ≥1030Elongation δ5 (%) : solid solution,≥20; Aging at 565℃,≥5; Aging at 510℃ ≥4Section shrinkage ratio ψ (%) : 565℃ aging,≥25; Aging at 510℃,≥10Hardness: solid solution,≤229HB; Aging at 565℃,≥363HB; Aging at 510℃,≥388HB

Heat treatment1.Solid solution,1000 ~ 1100℃ fast cooling;
2. Aged at 565℃, after solution treatment, 760±15℃ for 90min, cooled to below 15℃ within 1h, kept for 30min, then heated to 565±10℃ for 90min, air cooling;
3. 510℃ aging, after solid solution treatment,955±10℃ for 10min, air cooling to room temperature within 24h cooling to -73±6℃, maintained for 8h, then heated to 510±10℃ for 60min, air cooling.


Corrosion Resistance

---

The 631 stainless steel is highly corrosion-resistant in seawater, acids, and alkalis environments. It offers better corrosion resistance than 304 and 316 stainless steel due to its higher chromium content. However, the alloy is susceptible to pitting and crevice corrosion in chloride-containing solutions.


Why choose us

---

1.Size control 
2.Chemical composition control
4.ultrasonic testing of steel tube
3.hydraulic testing machine