PP Copolymer
Polypropylene
virgin&recycled
Specification:
Properties
Unit
Test method
Value
Melt Flow Rate
Melt flow rate(230°C/2.16KG)
g/10min
ISO 1133
12
Mechnical Properties
Tensile modulus of elasticity(v=1mm/min)
Mpa
ISO 527-2
1550
Tensile yield at stress(v=50mm/min)
Mpa
ISO 527-2
35
Tensile yield at strain (v=50mm/min)
%
ISO 527-2
8
Tensile strain at break (v=50mm/min)
%
ISO 527-2
>50
Charpy impact strength unnotched(+23°C)
kJ/m2
ISO 179/1eU
110
Charpy impact strength notched(+23°C)
kJ/m2
ISO 179/1eA
3.0
Izod Impact strength notenched(+23°C)
kJ/m2
ISO 180/1A
3
Ball indentation hardness(H 358/30)
Mpa
ISO 2039-1
78
Thermal Properties
Melting point,DSC
°C
ISO 3146
163
Heat deflection temperature ------------HDT/B(0.45Mpa)
°C
ISO 75-2
85
Vicat softening temperature ------------VST/A50(10N)
°C
ISO 306
154
Other Properties
Density
g/cm3
ISO 1183
0.91
PP Copolymer
Tests
Value
Unit
Melt Flow Rate
45
g/10min
Density
0.90
G/cm3
Elongation Stress
10
%
Flexural modulus
14
Mpa
Rockwell hardness
95
R scale
IZOD impact strength
6.5
kg.cm/cm
Vicat softening point
152
°C
Heat distortion temperature
125
°C
Packing
25kg in pp bag,20mt/1x20'FCL
PP Random Copolymer (PPR)
Tests
Value
Unit
Method
Melt Flow Rate (MFR)
0.45
g/10min
GB 3682
Density
0.91
g/cm3
ASTM D-1505
Tensile Strength at Yield
24
Mpa
GB 1040
Elongation at Break
750
%
GB 1040
Rockwellhardness
85
J/M
GB 9342
Izod impact strength
65
J/M
ASTM D-256
Packing
25kg in pp bag,20MT/1X20'FCL
Application:
Pipes
Transparent packaging
Houseware / household products/ household appliances
Fruit box
Beverage bottle
Microwave cooker
Water bottle
Detergent bottle
Personal care packaging
Advantage:
Light and billig health resistance to high temperature resistance wet, recycling easy
process molding, transparency and surface gloss, and mechanical properties of the higher good
non-toxic relative density low resistance to chemicals such good properties, and high ratio of performance